Abstrac The aim of the present study was to evaluate the cyclic fatigue, torsional resistance and surface roughness of Reciproc R25 instruments in four different situations, namely as new instruments and as instruments tested after clinical preparation of one, two or three maxillary molars with four root canals. The total time required to perform each root canal preparation was recorded. Cyclic fatigue resistance was determined by the time to fracture using a customized testing device (n = 10 per group). The torsional test evaluated the torque and angle of rotation to failure according to ISO 3630-1 (n = 10 per group). The roughness of the working parts of new and used instruments was evaluated with a profilometer (n = 5 per group). Statistical analysis was performed using one-way ANOVA and Tukey’s test. The level of significance was set at 5%. No fractures or deformations were observed after clinical use. Higher preparation time was needed during the third use of the instruments for all root canals (p < 0.05). There were no significant differences among the groups in regard to either cyclic fatigue or torsional resistance (p > 0.05). Regarding the roughness measurements, groove depth was higher on new and one- versus two- or three-maxillary-molar-prepared instruments (p < 0.05). It can be concluded that the clinical use of Reciproc instruments increased preparation time and decreased surface roughness. However, clinical use did not affect the cyclic fatigue or torsional resistance of the Reciproc instruments.

RESUMO Objetivo: Este estudo comparou a vida em fadiga de instrumentos endodônticos fabricados com a liga de NiTi convencional com eletropolimento de superfície, RaCe (FKG Dentaire, LaChauxdeFonds, Suiça), com instrumentos fabricados com a liga de NiTi CM Wire, submetidos a tratamento termomecânico, no processo de fabricação, HyFlex CM (Coltene Whaledent, Cuyahoga Falls, Ohio, EUA), ambos com geometria e dimensões semelhantes, visando determinar a influência do processo de fabricação das ligas e do acabamento superficial na resistência à fadiga. Métodos: Foram utilizados vinte instrumentos HyFlex CM e RaCe com D0 0,25mm, conicidade 0,06mm/mm, 25mm de comprimento, ambos com seção transversal triangular. A resistência à fratura foi avaliada através de teste estático de fadiga ciclica, utilizando um canal artificial em aço-inoxidável com 5mm de raio (86°), sendo registrado o tempo e calculado o número de ciclos para ocorrer a fratura (NCF). Para análise estatística empregou-se o teste t de Student. As superfícies de fratura dos instrumentos foram analisadas em MEV. Resultados: O NCF foi significativamente maior para os instrumentos HyFlex CM em comparação com as limas RaCe (p˂0,05), sendo 1336% mais resistentes à fadiga. A análise das superfícies fraturadas em MEV revelou características morfológicas do tipo dúctil para ambos os instrumentos e ausência de deformação plástica. Conclusão: Os instrumentos HyFlex CM apresentaram valores mais elevados de NCF. Deste modo, pode-se concluir que o tratamento térmico a qual estes instrumentos com a liga CM Wire foram submetidos os torna mais resistentes à fratura do que os instrumentos Race, fabricados com a liga de NiTi convencional com eletropolimento.

ABSTRACT Objective: This study compared the fatigue behavior of endodontic instruments manufactured with conventional NiTi alloy electropolishing, RaCe (FKG Dentaire, LaChauxdeFonds, Switzerland), with instruments manufactured with NiTi CM Wire subjected to thermomechanical treatment, in the manufacturing process, HyFlex CM (Coltène Whaledent, Cuyahoga Falls, Ohio, USA), both with similar geometry and dimensions in order to determine the influence of the manufacturing process in the fatigue resistance. Methods: The methodoly consisted of twenty HyFlex CM and RaCe instruments with D0 0.25 mm, taper 0.06 mm / mm, 25 mm length, both with triangular cross section. The fracture resistance was evaluated by static fatigue test, using a stainless artificial canal with 5mm of radius (86°), recording the time and calculating the number of cycles until fracture occurs (NCF). For statistical analysis the Student t test was used The fractured instruments surface was analyzed by SEM. Results: The NCF was significantly higher for HyFlex CM instruments in comparison with RaCe files (P˂0.05) being 1336% more resistant to fatigue. The analysis of the fractured surface by SEM showed ductile-kind morphological characteristics for both instruments and the absence of plastic deformation. Conclusion: HyFlex CM instruments present higher values of NCF. Thus, it can be concluded that the thermal treatment to which these instruments with CM Wire alloy are submitted makes them more resistant to fracture than Race instruments manufactured with conventional NiTi alloy electropolishing.

Resumo O objetivo do presente estudo foi avaliar a fadiga cíclica de dois instrumentos finalizadores anatômicos: XP-Endo Finisher e XP-Clean. O padrão de rugosidade e a micro dureza dos instrumentos também foram avaliados. Os instrumentos foram submetidos à resistência à fadiga cíclica, medindo o tempo de fratura em um canal artificial de aço inoxidável com um ângulo de 60 ° e um raio de curvatura de 5 mm. A superfície de fratura de todos os fragmentos foi examinada com um microscópio eletrônico de varredura. A rugosidade dos instrumentos foi quantificada usando um perfilômetro e o teste de micro dureza foi realizado usando um testador de dureza Vickers. Os resultados foram analisados estatisticamente usando o teste t de student em um nível de significância de p<0,05. A análise Weibull também foi realizada. XP-Endo Finisher apresentou vida de fadiga cíclica significativamente mais longa do que os instrumentos XP-Clean (p<0,05). XP-Endo Finisher foi capaz de suportar 1000% mais ciclos para fratura quando comparado aos instrumentos XP-Clean. A inspeção visual em microscópio eletrônico de varredura das superfícies de fratura revelou características fractográficas da fratura dúctil em todos os instrumentos testados. Não foi observada deformação plástica no eixo helicoidal dos instrumentos fraturados. Quando o tempo para a fratura foi comparado entre os instrumentos, o XP-Endo Finisher durou mais do que o XP-Clean com uma probabilidade de 99,9%. Os instrumentos XP-Endo Finisher também exibiram uma rugosidade significativamente menor do que os instrumentos XP-Clean (p<0,05). Não foram observadas diferenças na micro dureza entre os arquivos (p>0,05). Pode-se concluir que os instrumentos XP-Endo Finisher apresentaram desempenho melhorado em comparação com os instrumentos XP-Clean, demonstrando maior resistência à fadiga cíclica e menor rugosidade.

Abstract The aim of the present study was to evaluate the cyclic fatigue of two anatomic finishing files: XP-Endo Finisher and XP-Clean. Roughness pattern and the micro-hardness of the files were also assessed. Instruments were subjected to cyclic fatigue resistance measuring the time to fracture in an artificial stainless-steel canal with a 60° angle and a 5-mm radius of curvature. The fracture surface of all fragments was examined with a scanning electron microscope. The roughness of the working parts was quantified by using a profilometer and the micro-hardness test was carried out using a Vickers hardness tester. Results were statistically analyzed using a student´s t-test at a significance level of P < 0.05. Weibull analysis was also performed. XP-Endo Finisher presented significantly longer cyclic fatigue life than XP-Clean instruments (P<0.05). XP-Endo Finisher was able to withstand 1000% more cycles to fracture when compared to XP-Clean instruments. SEM visual inspection of the fracture surfaces revealed fractographic characteristics of ductile fracture in all tested instruments; wide-ranging forms of dimples were identified and no plastic deformation in the helical shaft of the fractured instruments was observed. When mean life was compared XP-Endo Finisher lasted longer than XP-Clean with a probability of 99.9%. XP-Endo Finisher instruments also exhibited significantly lower roughness than XP-Clean instruments (P<0.05). No differences in the micro-hardness was observed between the files (P>0.05). It can be concluded that XP-Endo Finisher instruments showed improved performance when compared with XP-Clean instruments, demonstrating higher cyclic fatigue resistance and lower roughness.